针对复合材料构件边角区域分层问题,提出了对分层区域分次打磨切除并重新粘接补片的修补方案。制备了复合材料层压板边角分层缺陷试样,对试样进行了无损探伤、拉伸和弯曲实验、显微检测,并对实验件的无损探伤结果、力学性能和显微结构进行分析。结果表明:修补后的试样无损检测合格,试样拉伸强度恢复率较好,试样弯曲强度恢复率完好。此方法为复合材料构件执行外场修补提供了一种快速有效的修补方法。并已在实际生产和外场排故中完成了初步的工程应用。
To solve the problem of corner delamination flaw of composite laminate components,proposed a repairing method that polished and cutted for several times,then re-bonding the patch.The sample of corner delamination flaw of composite laminate was prepared,the analysis of nondestructive testing,Mechanical properties,microscopic structure of the repaired sample were carried out.The result showed that,the nondestructive testing was qualified,tensile and the bending strength recovery rate of sample was better.In outfield troubleshooting,this method provided a quick and effective mean to repair composite components.And it had completed preliminary engineering application in actual production and outfield troubleshooting.
[1] Armstrong K B,Bevan L G,Cole W.Care and repair of advanced composites[M].UK:Society of Automotive Engineers,2005,27-29.
[2] 程小全.复合材料层合板与蜂窝夹芯板低速冲击后压缩性能研究[D].北京:北京航空航天大学,1998.
[3] 龚志红,包啸,李建川,等.中温固化复合材料层压板分层缺陷注射修补工艺研究[J].玻璃钢/复合材料,2017(6):85-88.
[4] 魏建义.航空复合材料结构修补技术与应用[J].橡塑技术与装备,2015(24):146-148.
[5] 苏建,田鹏飞.中温固化复合材料层压板分层缺陷挖补修补工艺研究[J].纤维复合材料,2017(3):3-7.
[6] Liu S,Cheng X,Xu Y,et al.Study on impact performance of scarf-repaired carbon firber carbon firber reinforced polymer laminates[J].Journal of Reinforced Plastics & Composites,2014,34(1):60-71.
[7] 喻梅,许希武.复合材料挖补修理结构的压缩强度分析[J].中国矿业大学学报,2008,37(5):709-714.
[8] 赵文漪,程小全,郭鑫.冲击位置对挖补修理层合板冲击后压缩性能的影响[J].高科技纤维与应用,2013,38(6):10-14.
[9] 王莹.复合材料缺陷修补技术[J].粘接,2015(6):83-86.
[10] Avery J L,Sonkar B V.Compressive failure of sandwich beams with debonded face-sheets[J].Journal of Composite Materials,2000,34(14):1176-1199.
[11] 蔡建丽,余欢,王云莹,等.玻璃钢蜂窝夹层结构制品常见缺陷修补技术[J].玻璃钢/复合材料,2011(1):28-31.
[12] 赵美英,孙晓波,万小朋.蜂窝夹芯结构板芯脱胶修补研究[J].航空学报,2003,24(5):474-476.
[13] 焦婷,杨胜春.复合材料粘接修理分析与验证技术研究[C].北京:第十七届全国复合材料学术会议,2012.
[14] 孙雨辰,季佳佳.航空复合材料结构修理方法[J].航空制造技术,2015,58(20):96-100.
[15] 郭彦江,黄俊,蒙志君.复合材料层合板贴补修理稳定性研究[J].玻璃钢/复合材料,2013(2):13-16.
[16] Goswami S,Becker W.The effect of facesheet/core delamination in sandwich structures under trasverse loading[J].Composites Strucetures,2011,54:515-521.
[17] 邹国发,龙国荣,万建平,等.树脂基复合材料蜂窝夹层结构修补技术研究[J].玻璃钢/复合材料,2005(6):2-44.
[18] 陈绍杰.复合材料结构修补技术与应用[J].塑胶技术与装备,2015(24):146-148.
[19] Das M,Madenci E,Ambur D R.Three-dimensional nonlinear analyses of scarf repair in composite laminates and sandwich panels[J].Journal of Mechanics of Materials & Structures,2008,3(9):1641-1658.
[20] Cheng X.Damage of scarf-repaired composite laminates subjected to low-velocity impacts[J].Steel & Composite Structures,2014,17(2):199-213.
PDF
(5940KB)